Wood Imitation blended polyol

Статус доступності:

A.Furniture 


ItemIndexIndex
Blowing AgentHCFC-141bHFC-245FA
Material Temperature20~25℃20~25℃
POL/ ISO Ratio1:1 ~1.2pbw1:1.1~1.2pbw
Mold Temperature40~45℃35~45℃
Cream Time15~40s15~25s
Gel Time70~160s70~100s
Tack Free Time90~210s100~130s
Free Rise Density80~120 kg/m380~110 kg/m3


*The actual reactivity characteristics may be adjusted according to process conditions and clients’requirements.

*Isocyanate is polymeric MDI


B.Line /Decoration

 

ItemIndexIndex
Blowing AgentHCFC-141bHFC-245FA
Material Temperature20~25℃20~25℃
POL/ ISO Ratio1:1 ~1.2pbw1:1.1~1.2pbw
Mold Temperature40~45℃35~45℃
Cream Time10~20s10~20s
Gel Time50~100s50~100s
Tack Free Time80~160s80~160s
Free Rise Density50~80 kg/m350~80 kg/m3


*The actual reactivity characteristics may be adjusted according to process conditions and clients’requirements.

*Isocyanate is polymeric MDI


C.PU trowel


ItemIndexIndex
Blowing AgentHCFC-141bWater
Material Temperature20~25℃20~25℃
POL/ ISO Ratio1:1pbw1:1.5pbw
Mold Temperature25℃25℃
Cream Time10-20s10-20s
Gel Time40-60s40-60s
Tack Free Time50-90s50-90s
Free Rise Density35-55 kg/m335-55 kg/m3


*The actual reactivity characteristics may be adjusted according to process conditions and clients’ requirements.

*Isocyanate is polymeric MDI